Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Specific Gravity比重
|
1.17 g/cc
|
1.17 g/cc
|
ASTM D792
|
|
Water Absorption吸水率
|
0.40 %
|
0.40 %
|
24 hours; ASTM D570
|
|
Linear Mold Shrinkage線性收縮率
|
0.0040 - 0.0080 cm/cm
|
0.0040 - 0.0080 in/in
|
ASTM D955
|
|
Melt Index of Compound熔體流動速率
|
5.5 g/10 min
@Load 3.80 kg, Temperature 230 °C |
5.5 g/10 min
@Load 8.38 lb, Temperature 446 °F |
ASTM D1238
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Hardness, Rockwell M羅氏硬度M
|
58
|
58
|
ASTM D785
|
|
Tensile Strength at Break斷裂拉伸強度
|
45.0 MPa
|
6530 psi
|
ASTM D638
|
|
Elongation at Break斷裂伸長率
|
80 %
|
80 %
|
ASTM D638
|
|
Flexural Strength彎曲強度
|
83.0 MPa
|
12000 psi
|
ASTM D790
|
|
Flexural Modulus彎曲彈性模量
|
2.167 GPa
|
314.3 ksi
|
ASTM D790
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度
|
0.392 J/cm
|
0.734 ft-lb/in
|
ASTM D256
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
>= 1.00e+15 ohm-cm
|
>= 1.00e+15 ohm-cm
|
ASTM D257
|
|
Dielectric Constant介電常數
|
3.5
@Frequency 60 Hz |
3.5
@Frequency 60 Hz |
ASTM D150
|
|
Dielectric Strength介電強度
|
15.0 kV/mm
|
381 kV/in
|
4kV/s; ASTM D149
|
|
Dissipation Factor耗散因數
|
0.040
@Frequency 60 Hz |
ASTM D150
|
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE, linear線性熱膨脹系數
|
60.0 μm/m-°C
@Temperature 20.0 °C |
33.3 μin/in-°F
@Temperature 68.0 °F |
ASTM D696
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
84.0 °C
|
183 °F
|
ASTM D648
|
|
Vicat Softening Point維卡軟化點
|
94.0 °C
|
201 °F
|
1 kg; ASTM D1525
|
|
Annealing Point退火點
|
60.0 - 70.0 °C
|
140 - 158 °F
|
3-5 hours
|
|
Optical Properties光學性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
ReFRactive Index折射率
|
1.49
|
1.49
|
ASTM D542
|
|
Haze霧度
|
1.0 %
@Thickness 3.20 mm |
1.0 %
@Thickness 0.126 in |
ASTM D1003
|
|
TRansmission, Visible透光率
|
92 %
@Thickness 3.20 mm |
92 %
@Thickness 0.126 in |
ASTM D1003
|
|
Processing Properties加工性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Processing Temperature加工溫度
|
210 - 250 °C
|
410 - 482 °F
|
Injection molding cylinder temperature
|
|
Mold Temperature模具溫度
|
60.0 - 70.0 °C
|
140 - 158 °F
|
|
|
Drying Temperature干燥溫度
|
60.0 - 70.0 °C
|
140 - 158 °F
|
|
|
Dry Time干燥時間
|
4 - 6 hour
|
4 - 6 hour
|
|
|
Injection Pressure注射壓力
|
49.03 - 107.87 MPa
|
7111 - 15645 psi
|
溫馨提示您:
因塑膠原料行情每天每時波動較大無法及時更新，導致頁面上報價可能會與當天實際報價有所差異，請親們理解及時來電咨詢！
電話：鄧行秀女士0769-33327260或15817520076
公司：東莞市勝浩塑膠原料有限公司（樟木頭恒泰塑膠經營部）
地址：東莞市樟木頭鎮先威大道塑膠商務中心7棟56號
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換