PA66 A3X2G7 德國巴斯夫公司 物性數據 |
|
①原料描述部分 |
||||||
②原料技術數據 |
|||||||
性能項目 |
試驗條件[狀態(tài)] |
測試方法 |
測試數據 |
數據單位 |
|||
機械性能 |
拉伸彈性模量 |
干/濕 |
--- |
11000/8500 |
MPa |
||
拉伸屈服應力(V=50mm/min) |
干/濕 |
--- |
160/120 |
MPa |
|||
斷裂應力(V=50mm/min) |
干/濕 |
--- |
160/120 |
MPa |
|||
屈服伸長率(V=50mm/min) |
干/濕 |
--- |
3/4 |
% |
|||
斷裂伸長率(V=50mm/min) |
干/濕 |
--- |
3/4 |
% |
|||
拉伸蠕變模量 |
1000h,濕 |
--- |
4250 |
MPa |
|||
伸長率 |
≤0.5%, +23℃,濕 |
--- |
4250 |
MPa |
|||
彎曲模量 |
干/濕 |
--- |
9200 |
MPa |
|||
卡畢沖擊強度 |
+23℃,干/濕 |
--- |
70/70 |
KJ/m2 |
|||
卡畢沖擊強度 |
30℃,干 |
--- |
65 |
KJ/m2 |
|||
卡畢缺口沖擊強度 |
+23℃,干/濕 |
--- |
14/18 |
KJ/m2 |
|||
埃佐缺口沖擊強度 |
+23℃,干/濕 |
--- |
13/20 |
KJ/m2 |
|||
沖擊、破壞能量 |
+23℃,干/濕 |
--- |
2/10 |
J |
|||
球壓硬度 |
干/濕 |
--- |
210 |
MPa |
|||
電氣性能 |
介電常數 |
1MHz,干/濕 |
--- |
3.6/5 |
--- |
||
損耗角 |
1MHz,干/濕 |
--- |
0.02/0.2 |
--- |
|||
體積電阻 |
干/濕 |
--- |
1015/1012 |
Ω.cm |
|||
表面電阻 |
干/濕 |
--- |
>1013/1010 |
Ω |
|||
介電強度 |
K20/P50,干/濕 |
--- |
70/40 |
KV/mm |
|||
對電弧徑跡指數CT1 |
干/濕 |
--- |
CTI 600 |
--- |
|||
相對電弧徑跡指數CTIM |
干/濕 |
--- |
CTI 600 M |
--- |
|||
熱 性 能 |
比熱容 |
干態(tài) |
--- |
1.4 |
J/(g.K) |
||
大使用溫度 |
--- |
--- |
220 |
℃ |
|||
溫度指數 |
在20000h/5000h,后拉伸強度下降50%時 |
--- |
140/157 |
℃ |
|||
線性熱膨脹系數 |
(23-80)℃,干態(tài) |
--- |
1.5-2/6-7 |
10-5/K |
|||
導熱率 |
干態(tài) |
--- |
0.34 |
W/(m.K) |
|||
熱變形溫度 |
1.8MPa負荷,干態(tài) |
--- |
250 |
℃ |
|||
熱變形溫度 |
0.45MPa負荷,干態(tài) |
--- |
250 |
℃ |
|||